Syncoat Chemicals (2017) Ltd.’s Primer Technologies are completely compatible with any of our products. We offer a variety of both solvent and water based technologies.
Solvent Based Epoxy Primer
- Two component
- VOC – 400 grams per litre
- Forms a hard cross-linked film with excellent solvent, chemical, and heat resistance
- Exceptional corrosion resistance
- Has been designed for a variety of top coats where very good corrosion resistance is needed
- Preferred pre-treatment is our Iron Phosphate Systems
| Test | Result |
|---|---|
| Adhesion | 5B |
| Hardness | 2-4 H |
| Solvent Resistance | 200 double rubs MEK |
| Gloss | Satin Finish |
| Humidity Resistance (ASTM D1735) | 500 Hours No face blisters or corrosion |
| CORROSION RESISTANCE | |
| GMW14872 42 Cycles Under Syncoat NISO | Less than 2 mm creep from the scribe. No face blistering or corrosion |
| Salt Spray 500 Hours ASTM B117 Under Syncoat NISO | Less than 1 mm creep from the scribe. No face blistering or corrosion |
Water Based Epoxy Primer
- Two component
- Low VOC – 100 grams per litre
- HAPS free
- Forms a cross linked film with excellent chip and corrosion resistance
- Excellent heat, chemical, and solvent resistance as a stand-alone product
- For use under top coats that require a finish with superior performance
| Test | Result |
|---|---|
| Adhesion | 5B |
| Hardness | HB-F |
| Gloss | Flat Finish |
| Flexibility ASTM D522 | Passes 1/8” |
| Humidity Resistance ASTM D1735 | 500 Hours No face blistering or corrosion |
| CORROSION RESISTANCE | |
| GMW14872 42 Cycles | Less than 4 mm creep from the scribe No face blistering or corrosion |
| SCAB ISO 11474 | Less than 4 mm creep from the scribe No face blistering or corrosion |
Solvent Based Alkyd Primer
- Single component
- VOC – 423 grams per litre
- Fast drying
- Heat resistant
- Anti-corrosive
| Test | Result |
|---|---|
| Application | Air-spray, HLVP, Airless, Dip, Brush |
| Gloss | Flat Finish |
| Chip Resistance (SAE J400) | 4B Maximum, Flat pieces from production intent components |
| CORROSION RESISTANCE | |
| GMW14872 35 Cycles | Scribe rating of 6 (<3.0mm failure at scribe) as per ASTM D1654 |
| Heat Resistance GMW14872 Cyclic Testing | 3 cycles of 6 hours at 300°F 35 cycles - Scribe rating of 6 (<3.0mm failure at scribe) as per ASTM D1654 |